Cable Jointing Compound suitable upto 33kv.
Jala Compound for [ Telecombination Joint ]
Cable compounds manufactured by us are a two component, cold cured system.
The compounds has to be mixed in the ratio of 5 : 1.
The general properties of
the system are moderate exotherm, low shrinkage,excellent
impact, heat and shock
resistance, no settling of compound on long storage,
resistance to dilute acids, alkalies,
organic solvents and transformer oil.
The compound is ideally used in cable jointing kits for
XLPE/PVC/PILC cables,
both for
low tension and high tension.
PROPERTIES :
| Pot
life |
: |
30 minutes at 30 deg.c |
|
Curing
time |
: |
40 to 60 minutes at 30 deg.c |
|
Water
absorption |
: |
0.25 % (after mixing) |
|
Density |
: |
1.32gm/ml. (after mixing) |
|
Tensile strength Kgf/cm2 |
: |
273 |
|
Elongation at break
% |
: |
30 |
|
Tracking
Resistance |
: |
600 |
|
DI electric Strength |
: |
15kv/mm |
| Dissipation
factor |
: |
0.03 (at 27 Deg. c) |
|
Permitivity |
: |
5 (at 27 Deg.c) |
|
Volume resistivity |
: |
3x 10 - 1x 10 ohm - cm. |
|
DI-electric
constant |
: |
5.5 |
We also manufacture cable jointing compounds in 3 part system i.e. Resin,
Hardener and
Filler packed separately in bucket packs and also in two parts packed in pouch.
|